扣件的技术要求
Release time：
2020-08-11 16:18
source：
十字扣件厂家应按规定程序批准的图样进行生产。扣件铸件的材料应采用GB/T 9440中所规定的力学性能不低于KTH 330-08 牌号的可锻铸铁或GB/T 11352中ZG 230-450铸钢。扣件在主要部位不得有缩松、夹渣、气孔等铸造缺陷。扣件应严格整形，与钢管的巾和面应紧密接触，应保证扣件抗滑、抗拉性能。扣件（除底座外）应经过65N·m扭力矩试压，扣件各部位不应有裂纹。扣件用脚手架钢管应采用GB/T3091中公称外径为48.3mm的普通钢管，其公称外径、壁厚的允许偏差及力学性能应符合GB/T3091的规定。
扣件用T型螺栓、螺母、铆钉采用的材料应符合GB/ T867的规定.T型螺栓M12,其总长应为(72±0.5)mm,螺母对边宽应为(22±0.5)mm,厚度应为(14±0.5)mm；铆钉直径应为(8±0.5)mm,铆接头应大于铆孔直径1mm；旋转扣件中心铆钉直径应为(14±0.5)mm.
外观和附件质量要求：各部位不应有裂纹。盖板与座的张开距离不得小于50mm；当钢管公称外径为51mm时，不得小于55mm。表面大于10
的砂眼不应超过3处，且累计面积不应大于50。扣件表面粘砂面积累计不应大于150。错箱不应大于1mm.
扣件表面凹(或凸)的高（或深）值不应大于1mm。扣件与钢管接触部位不应有氧化皮，其他部位氧化皮面积累计不应大于150。铆接处应牢固，不应有裂纹。T型螺栓和螺母应符合GB/T3098.1、GB/T3098.2的规定。活动部位应灵活转动，旋转扣件两旋转面间隙应小于1mm。产品的型号、商标、生产年号应在醒目处铸出，字迹、图案应清晰完整。扣件表面应进行防锈处理（不应采用沥青漆），油漆应均匀美观，不应有堆漆或露铁。